Mechanical Properties from Epoxy-Laminates with TFP-Structures
| fibre volume fraction φ = 0,6 |
E-Glass/Epoxy | Tenax HTS 5131 / PR 500 | |||
|---|---|---|---|---|---|
| UD | UD | 0° / 90° | |||
| Tension | Young´s Modulus (GPa) |
44 | 142 | 64 | |
| Strength (MPa) |
960 | 2209 | 930 | ||
| Flexural | Young´s Modulus (GPa) |
35 | 124 | 100 | |
| Strength (MPa) |
1280 | 1730 | 1050 | ||
| Compression Strength (Celanese) (MPa) |
820 | 1280 (l = 10 mm) 1415 (l = 8 mm) |
|||